1: \documentclass[twocolumn,showpacs,preprintnumbers,amsmath,amssymb,prb,aps]{revtex4}
2: %\documentclass[preprint,onecolumn,showpacs,preprintnumbers,amsmath,amssymb,prb,aps]{revtex4}
3:
4: \usepackage{epsfig}% Include figure files
5: \usepackage{graphicx}% Include figure files
6: \usepackage{dcolumn}% Align table columns on decimal point
7: \usepackage{bm}% bold math
8:
9: \begin{document}
10:
11: \title{Electronic and structural transition in La$_{0.2}$Sr$_{0.8}$MnO$_3$}
12:
13: \author{R. Bindu and Kalobaran Maiti}
14: \affiliation{Department of Condensed Matter Physics and Materials
15: Science, Tata Institute of Fundamental Research, Homi Bhabha Road,
16: Colaba, Mumbai - 400 005, INDIA.}
17:
18: \author{R. Rawat}
19: \affiliation{UGC-DAE Consortium for Scientific Research, University
20: Campus, Khandwa Road, Indore 452 017, India.}
21:
22: \author{S. Khalid}
23: \affiliation{National Synchrotron Light Source, Brookhaven National
24: Laboratory, Upton, New York - 11973}
25:
26: \date{\today}
27:
28: \begin{abstract}
29:
30: We investigate the interplay of the electronic and structural
31: transition in La$_{0.2}$Sr$_{0.8}$MnO$_{3}$. The transport and
32: specific heat measurements exhibit unusual evolutions and signature
33: of a first order phase transition around 265 K. Mn K-edge extended
34: $x$-ray absorption fine structure results reveal distortion in the
35: MnO$_6$ octahedra even in the cubic phase and a remarkable evolution
36: of the distortion across the phase transition. These results
37: manifest the importance of fluctuations in Mn 3$d$ orbital occupancy
38: and disorder in their electronic properties, which may help in
39: understanding the orbital and spin ordering proposed in these
40: systems.
41:
42: \end{abstract}
43:
44: \pacs{61.50.Ks, 75.30.Kz, 75.47.Lx, 61.05cj}
45:
46: \maketitle
47:
48: %\section{Introduction}
49:
50: Discovery of colossal magnetoresistance (CMR) in manganites have
51: opened up a new field of research in solid state physics due to
52: their interesting fundamental issues and significant technological
53: applications such as high density storage media, field sensors, {\it
54: etc}. These systems exhibit plethora of exotic properties such as
55: charge, orbital and spin ordering, electronic phase separation, {\it
56: etc.} in addition to the CMR effect. It is now realized that the
57: intricate competition between the charge, spin, orbital, and lattice
58: degrees of freedom in these mixed valent manganites are important
59: for these exotic properties.\cite{coey,salamon,dagotto}
60:
61: Among all the manganites, La$_{1-x}$Sr$_{x}$MnO$_{3}$ ($x <$ 0.5) is
62: studied the most due to its proximity to the CMR effect. With the
63: increase in $x$, the tolerance factor becomes close to unity and the
64: Mn-O-Mn angle also becomes close to 180$^o$. In this situation, Mn
65: $e_{g}$ orbitals would be almost degenerate\cite{brink,ryo} and is
66: ideal to study the electronic charge distribution in Mn 3$d$ levels
67: across the electronic phase transitions observed in these systems.
68:
69: In this paper, we report our results on the electronic and
70: structural evolution associated to MnO$_6$ octahedra in
71: La$_{0.2}$Sr$_{0.8}$MnO$_3$ as a function of temperature. This
72: compound exhibits a transition from paramagnetic to C-type
73: antiferromagnetic (C-AFM) structure around 265 K.\cite{ch} Reports
74: on structural transition are controversial suggesting a cubic to
75: tetragonal\cite{ch} or no structural transition\cite{hem} with
76: temperature. Subsequent theoretical studies\cite{brink,ryo} predict
77: importance of orbital degeneracy in this system. The orbital
78: degeneracy of Mn 3$d$ states strongly depends on the local crystal
79: structure of the MnO$_6$ octahedra, which can be probed efficiently
80: by extended $x$-ray absorption fine structure (EXAFS) technique.
81: Thus, we have employed Mn K-edge EXAFS around the region of
82: electronic phase transition to investigate the evolution of the
83: local structural parameters of the MnO$_6$ octahedra. Our results
84: reveal that the MnO$_{6}$ octahedra are distorted even in the cubic
85: phase. The results at lower temperatures manifest phenomenal
86: evolution of the Mn-O bond lengths across the phase transition.
87:
88: %\section{Experimental and data analysis}
89:
90: The sample was prepared by conventional solid state route
91: \cite{EPJB} and characterized by powder $x$-ray diffraction
92: technique. Sample was found to be in single phase with no signature
93: of impurity feature. The analysis of the diffraction peaks at room
94: temperature indicates cubic structure with space group {\it
95: Pm$\overline{3}$m}. Iodometric redox titration confirmed the sample
96: to be stoichiometric. The resistivity and heat capacity measurements
97: were performed using standard four probe method and home made semi
98: adiabatic heat pulse calorimeter, respectively. Mn K-edge EXAFS
99: studies were carried out at X-18B beamline at the National
100: Synchrotron Light Source, Brookhaven National Laboratory with an
101: eneregy resolution of 0.8 eV at Mn K-edge.
102:
103: EXAFS analysis was carried out using UWXAS software\cite{stern}
104: following the standard procedure.\cite{xray} The Fourier transform
105: (FT) to the $R$-space was carried out in the $k$-range 3 - 13
106: \AA$^{-1}$ by Fourier transforming $k^{2}\chi(k)$ ($\chi(k)$ is the
107: EXAFS oscillations) by a Hanning window function. The back
108: scattering amplitude and phases were calculated using FEFF6.01a
109: code\cite{zabinsky} for LaMnO$_{3}$ and the same were used for all
110: the temperatures. The first coordination shell fit was done in the
111: Fourier filtered $k$-space in the range 0.86 - 1.87 \AA. The overall
112: many body reduction factor, $S_0^2$ was fixed to 0.82. As seen
113: earlier\cite{JPCM}, we find that the Mn K-edge EXAFS data at room
114: temperature are best described by 2 short Mn-O bond lengths, $R_1$
115: and 4 long Mn-O bond lengths, $R_2$. In order to avoid uncertainty
116: in the fitting procedure, we have considered average bond distances
117: for eight Mn-Sr/La bonds and six Mn-Mn bonds in higher coordination
118: shells (0.86 - 3.87 \AA).
119:
120: %\section{Results and Discussions}
121:
122: The temperature dependent resistivity, $\rho$ and heat capacity,
123: $C_p$ are plotted in Fig. 1. $\rho$ in Fig. 1(a) exhibits insulating
124: temperature dependence along with a sharp increase at about 265 K
125: ($T_1$) and a change of slope at about 254 K. In addition, a
126: distinct hysteresis is observed around $T_1$ and 224 K ($T_2$) for
127: the cooling and warming cycles. This is demonstrated in Fig. 1(b),
128: where we show the difference in $\rho$ between cooling ($\rho_c$)
129: and warming ($\rho_w$) cycles normalized by $\rho_c$. It is evident
130: that $(\rho_c - \rho_w)/\rho_c$ exhibits two peaks of opposite signs
131: at around $T_1$ and $T_2$. The change in sign suggests significant
132: modification in transport mechanisms at different temperatures. The
133: hysteresis observed in resistivity is an indication of first order
134: phase transition. Notably, the transition from paramagnetic to
135: C-type antiferromagnetic phase\cite{ch} is also observed at $T_1$.
136:
137: The heat capacity data shown in Fig. 1(c) exhibit a sharp peak at
138: $T_1$. The magnetic entropy change at this transition obtained by
139: subtracting the polynomial background is found to be very large, 4.3
140: J/mol.K. No distinct feature is observed around $T_2$.
141: Interestingly, at low temperatures, $C_p/T$ exhibit a linear
142: dependence with $T^2$ as shown in Fig. 1(d). Considering $C_p/T =
143: \gamma +\beta T^2$, the value of $\gamma$ is found to be 5.6
144: mJ/mol.K$^{2}$. In metals, $\gamma$ corresponds to the electronic
145: contribution to $C_p$. However, the compound in this study exhibits
146: insulating temperature dependence. Thus, the observation of large
147: $\gamma$ indicating finite density of states at the Fermi level is
148: unusual and needs further study to understand this effect.
149:
150: In Fig. 2(a), we show the temperature evolution of the modulus of
151: FT[k$^{2}$$\chi$(k)]. The FT curves are uncorrected for the central
152: and back scattering phase shifts. The figure shows three prominent
153: peaks around 1.5, 2.9 and 3.4 \AA\ marked by A, B and C,
154: respectively. Peaks A and B correspond to Mn-O and Mn-Sr/La shells,
155: respectively, and peak C corresponds to Mn-Mn and multiple
156: scattering paths (Mn-O-Mn). While there is no apparent shift in the
157: peak position of the peaks B and C, their relative intensity
158: decreases with the decrease in temperature as shown by plotting the
159: maxima of B and C in Fig. 2(b). At $T >$ 270 K, the peak B is weaker
160: than peak C. For 270 K $> T >$ 230 K, the intensities are very
161: similar and at $T <$ 230 K, the intensity of peak B increases
162: significantly relative to the intensity of peak C. Peak A exhibits a
163: small shift towards the origin and an increasing trend in intensity
164: with the decrease in temperature. Since, $\chi(k)$ is a function of
165: bond length, $R_j$ and Debye-Waller factor, $\sigma_j$ for the
166: $j$-th coordination shell, such modification in FT amplitude
167: indicates significant changes in these two parameters with
168: temperatures. In order to obtain the detailed structural information
169: of these modifications, we have carried out the EXAFS fitting on
170: Mn-O, Mn-Sr/La and Mn-Mn coordination shells. Representative fit of
171: these shells are shown in Fig. 2(c) and 2(d). The typical R-factors
172: for the first and higher coordination shell fits are 0.003 and
173: 0.015, respectively.
174:
175: First, we start with the first coordination shell corresponding to
176: Mn-O bonds. This shell is fitted with 2 short bonds, $R_1$ and 4
177: long bonds, $R_2$ and the results are shown in Fig. 3(a). It is
178: evident from the figure that the distribution in Mn-O bonds persists
179: with the decrease in temperature until 270 K. Interestingly, around
180: the region of phase transition ($\sim$ 265 K), R$_{1}$ and R$_{2}$
181: are almost identical indicating an undistorted MnO$_{6}$ octahedron.
182: At low temperatures, $R_1$ becomes significantly smaller than $R_2$
183: thereby MnO$_{6}$ octahedra become distorted. This is remarkable and
184: reveals presumably for the first time such behavior as a function of
185: temperature across a first order phase transition. This suggests
186: that tetragonal distortion starts from a perfectly cubic structure,
187: where the MnO$_6$ octahedra are also symmetric. A magnetic phase
188: transition (from PM to C-AFM) also occurs at $T_1$. Interestingly,
189: in sharp contrast to the common belief, the Mn-atoms corresponding
190: to the shorter bond length, $R_1$ becomes ferromagnetically coupled
191: and the ones with the longer bond lengths, $R_2$ are
192: antiferromagnetically coupled.
193:
194: When the MnO$_6$ octahedra are symmetric, the $d_{xy}$, $d_{yz}$ and
195: $d_{xz}$ orbitals are degenerate forming a $t_{2g}$ band, and
196: $d_{x^2-y^2}$ and $d_{z^2}$ orbitals are degenerate forming an $e_g$
197: band. In the ionic configuration, Mn 3$d$ bands in
198: La$_{0.2}$Sr$_{0.8}$MnO$_3$ have 3.2 electrons and the up spin
199: $t_{2g}$ band will be completely filled. The structural changes in
200: the MnO$_6$ octahedra will lead to a change in the degeneracy of the
201: $t_{2g}$ and $e_g$ bands, and hence significant fluctuation in
202: occupancy of $d_{x^2-y^2}$ and $d_{z^2}$ orbitals. Since, the
203: octahedra are compressed along apical direction ($R_1$; say
204: $z$-direction), the $d$ orbital corresponding to the plane having
205: larger Mn-O bond lengths ($R_2$; $d_{x^2-y^2}$) will be more
206: populated compared to the perpendicular one. This is presumably the
207: reason for the anomalous magnetic coupling observed in this system
208: as filled up spin $d_{x^2-y^2}$ band favors antiferromagnetic
209: coupling due to superexchange interaction.
210:
211: In order to explore plethora of unusual effects such as the sharp
212: peak in $C_p$, a steep increase in resistivity and the nucleation of
213: unusual magnetic coupling at $T_1$ further, we show the Debye-Waller
214: factors corresponding to $R_1$ and $R_2$ in Fig. 3(d) and 3(f). The
215: Debye-Waller factor corresponding to $R_1$ shown in Fig. 3(d) is
216: significantly large. This suggests strong influence of disorder in
217: localizing the Mn-O hybridized electronic states corresponding to
218: $R_1$. This is presumably the reason for insulating transport
219: despite the fact that ferromagnetic coupling along $R_1$ often
220: favors metallic conduction and finite $\gamma$ corresponds to finite
221: density of states at the Fermi level.
222:
223: In Figs. 3(b) and 3(c), we show the Mn-Sr/La and Mn-Mn bond lengths,
224: respectively and corresponding Debye-Waller factors are shown in
225: Fig. 3(e) and 3(f), respectively. It is evident from the figures
226: that around T$_{1}$, the average Mn-Sr/La and Mn-Mn bond lengths
227: remain almost the same.
228:
229: At 245 K, MnO$_{6}$ octahedra are the most distorted ones and the
230: Mn-Mn distance also becomes minimum. Below this temperature, the
231: distortion in MnO$_6$ octahedra reduces gradually with the decrease
232: in temperature and subsequently, the Mn-Mn distance also increases
233: gradually. The Debye-Waller factor corresponding Mn-Mn distance does
234: not change significantly (see Fig 3(f)) and that corresponding to
235: Sr/La atoms around Mn shown in Fig. 3(e) exhibits a gradual decrease
236: with temperature. This indicates that the disorder in Sr-sublattice
237: may not have significant role in the electronic properties of this
238: compound.
239:
240: Around T$_{1}$, the value of resistivity during warming cycle
241: ($\rho$$_{w}$) is more than the resistivity during cooling cycle
242: ($\rho$$_{c}$). Below 257 K, the value of $\rho$$_{c}$ becomes more
243: than $\rho$$_{w}$ and a change in slope is also observed. Such
244: unusual modification in transport behavior presumably due to the
245: temperature induced structural evolution of the MnO$_6$ octahedra
246: leading to fluctuation of the occupancy of the Mn $e_g$ orbitals in
247: the presence of strong disorder.
248:
249: %\section{Conclusions}
250:
251: In summary, we have studied the electronic properties of
252: La$_{0.2}$Sr$_{0.8}$MnO$_{3}$ using resistivity and heat capacity
253: measurements. Transport and heat capacity data reveal a first order
254: phase transition around 265 K. The local structure was probed by Mn
255: K-edge EXAFS technique. The MnO$_6$ octahedra are found to be
256: distorted even in the cubic phase at room temperature. EXAFS results
257: at different temperatures manifests remarkable evolution of the
258: MnO$_6$ octahedra across the first order phase transition. We
259: observe that the tetragonal distortion and the antiferromagnetic
260: ordering nucleates from a perfectly cubic structure, where the
261: MnO$_6$ octahedra are symmetric. Thus, the phase transition in this
262: compound involves significant fluctuation in the Mn 3$d$ orbital
263: occupancy and disorder induced localization, which may be important
264: in understanding interesting orbital and spin ordering observed in
265: manganites.
266:
267: \pagebreak
268:
269: \begin{thebibliography}{99}
270:
271: \bibitem{coey}J. M. D. Coey, M. Viret and S. von Moln$\acute{a}$r,
272: Adv. Phys. {\bf 48}, 167 (1999).
273:
274: \bibitem{salamon} M. B. Salamon and M. Jaime, Rev. Mod. Phys. {\bf 73}, 583
275: (2001).
276:
277: \bibitem{dagotto} E. Dagotto, T. Hotta, A. Moreo, Physics Reports. {\bf 344}, 1
278: (2001).
279:
280: \bibitem{brink} J. van den Brink, G. Khaliullin, and D. Khomskii,
281: Phys. Rev. Lett. {\bf 83}, 5118 (1999).
282:
283: \bibitem{ryo} R. Maezono, S. Ishihara and N. Nagaosa,
284: Phys. Rev. B. {\bf 58}, 11583 (1998).
285:
286: \bibitem{ch} O. Chmaissem, B. Dabrowski, S. Kolesnik, J. Mais, J. D. Jorgensen
287: and S. Short, Phys. Rev. B {\bf 67}, 094431 (2003).
288:
289: \bibitem{hem} J. Hemberger, A. Krimmel, T. Kurz, H. -A. Krug von Nidda, V. Yu. Ivanov, A. A. Mukhin, A. M. Balbashov, and A. Loidl, Phys. Rev.
290: B. {\bf 66}, 094410 (2002).
291:
292: \bibitem{EPJB} R. Bindu, Eur. Phys. J. B. {\bf 37}, 321 (2004).
293:
294: \bibitem{stern} E. A. Stern, M. Newville, B. Ravel, Y. Yacoby, D. Haskel,
295: Physica B. {\bf 208}, 117 (1995).
296:
297: \bibitem{xray} \emph{X}-ray absorption: Principles, Applications, Techniques
298: of EXAFS, SEXAFS and XANES, edited by D. C. Konningsberger and R.
299: Prins (John Wiley and Sons, New York, 1988).
300:
301: \bibitem{zabinsky} S. I. Zabinsky, J. J. Rehr, A. Ankudinov, R. C. Albers
302: and M. J. Eller, Phys. Rev. B. {\bf 52}, 2995 (1995).
303:
304: \bibitem{JPCM} R. Bindu, S. K. Pandey, A. Kumar, S. Khalid and A. V. Pimpale,
305: J. Phys: Cond. Matt. {\bf 17}, 6393 (2005).
306:
307:
308: \end{thebibliography}
309:
310:
311: \pagebreak
312:
313: \section{Figure Captions:}
314:
315: Fig. 1: (color online) (a) The resistivity during warming (open
316: circles), cooling (line) cycles. (b) The difference in the
317: resistivity during the cooling ($\rho$$_{c}$) and warming
318: ($\rho$$_{w}$) cycles normalized by $\rho_c$. (c) The heat capacity,
319: $C_p$ as a function of temperature. (d) $C_p/T$ vs $T^2$ ($T$ =
320: temperature) shown in the low temperature region.
321:
322: Fig. 2: (color online) (a) The Fourier transform (FT) of $k^2
323: \chi(k)$ at different temperatures. (b) The intensities of the peaks
324: A, B and C as a function of temperature. Representative fits for the
325: case of (c) first and (d) higher coordination shells at 255 K. The
326: open circles and the solid line indicate the experimental and the
327: fitted patterns respectively.
328:
329: Fig. 3: (color online) The variation of (a) $R_1$ and $R_2$, (b)
330: Mn-Sr/La and (c) Mn-Mn bond lengths as a function of temperature
331: obtained from EXAFS fitting. The Debye-Waller factors corresponding
332: to (d) $R_1$, (e) Sr/La, and (f) $R_2$ and Mn as a function of
333: temperature.
334:
335: \end{document}