1: \begin{abstract}

2: A comprehensive phase diagram of lowest-energy structures and compositions

3: of the rutile TiO$_2$(110) surface in equilibrium with a surrounding gas

4: phase at finite temperatures and pressures has been determined using density

5: functional theory in combination with a thermodynamic formalism. The exchange

6: of oxygen, hydrogen, and water molecules with the gas phase is considered.

7: %

8: Particular attention is given to the convergence of all calculations with

9: respect to lateral system size and slab thickness. In addition, the

10: reliability of semilocal density functionals to describing the energetics

11: of the reduced surfaces is critically evaluated. 

12: %

13: For ambient conditions the surface is found to be fully covered by

14: molecularly adsorbed water. At low coverages, in the limit of single,

15: isolated water molecules, molecular and dissociative adsorption become

16: energetically degenerate.

17: %

18: Oxygen vacancies form in strongly reducing, oxygen-poor environments.

19: However, already at slightly more moderate conditions it is shown that

20: removing full TiO$_2$ units from the surface is thermodynamically preferred.

21: %

22: In agreement with recent experimental observations it is furthermore

23: confirmed that even under extremely hydrogen-rich environments the surface

24: cannot be fully hydroxylated, but only a maximum coverage with hydrogen of

25: about 0.6--0.7 monolayer can be reached.

26: %

27: Finally, calculations of migration paths strongly suggest that hydrogen

28: prefers to diffuse into the bulk over desorbing from the surface into the

29: gas phase. 

30: %

31: \end{abstract}