2: We investigated the iron-based ladder compounds (Ba,Cs)Fe$_2$Se$_3$. Their parent compounds, BaFe$_2$Se$_3$ and CsFe$_2$Se$_3$, have different space groups, formal valences of Fe and magnetic structures.

3: Electrical resistivity, specific heat, magnetic susceptibility, X-ray diffraction and powder neutron diffraction measurements were conducted to obtain temperature and composition phase diagram of this system.

4: Block magnetism observed in BaFe$_2$Se$_3$ is drastically suppressed with Cs doping.

5: In contrast, stripe magnetism observed in CsFe$_2$Se$_3$ is not so fragile against Ba doping.

6: New type of magnetic structure appears in intermediate compositions, which is similar to stripe magnetism of CsFe$_2$Se$_3$, but inter-ladder spin configuration is different.

7: Intermediate compounds show insulating behavior, nevertheless finite $T$-linear contribution in specific heat was obtained at low temperatures.