2: The crystal and magnetic structures and underlying magnetic interactions of Bi$_4$Fe$_5$O$_{13}$F, a model system for studying the physics of the Cairo pentagonal spin lattice, are investigated by transmission electron microscopy, low-temperature synchrotron x-ray and neutron powder diffraction, thermodynamic measurements, and density functional band-structure calculations. The crystal structure of Bi$_4$Fe$_5$O$_{13}$F contains infinite rutile-like chains of edge-sharing FeO$_6$ octahedra interconnected by the Fe$_2$O$_7$ groups of two corner-sharing FeO$_4$ tetrahedra. The cavities between the chains are filled with the fluorine-centered Bi$_4$F tetrahedra. The Fe$^{3+}$ cations form pentagonal units that give rise to an unusual topology of frustrated exchange couplings and underlie a sequence of the magnetic transitions at $T_1$ = 62~K, $T_2$ = 71~K, and $T_N$ = 178~K. Below $T_1$, Bi$_4$Fe$_5$O$_{13}$F forms a fully ordered non-collinear antiferromagnetic structure, whereas the magnetic state between $T_1$ and $T_N$ may be partially disordered according to the sizable increase in the magnetic entropy at $T_1$ and $T_2$. Therefore, Bi$_4$Fe$_5$O$_{13}$F shows the evidence of intricate magnetic transitions that were never anticipated for the pentagonal Cairo spin lattice. Additionally, it manifests a sillimanite (Al$_2$SiO$_5$)-based homologous series of compounds that feature the pentagonal magnetic lattice spaced by a variable number of octahedral units along the rutile-type chains.

3: \end{abstract}

4: