1: \begin{abstract}

2: Tin-chalcogenides SnX (X = Te, Se and S) have been arousing research interest

3: due to their thermoelectric physical properties. The two-dimensional (2D)

4: counterparts, which are expected to enhance the property, nevertheless, have

5: not been fully explored because of many possible structures. Generating variable

6: composition of 2D Sn$_{1-x}$X$_{x}$ systems (X = Te, Se and S) has been performed

7: using global searching method based on evolutionary algorithm combining

8: with density functional calculations. A new hexagonal phase named by $\beta'$-SnX

9: is found by Universal Structure Predictor Evolutionary Xtallography (USPEX), and

10: the structural stability has been further checked by phonon

11: dispersion calculation and the elasticity criteria. The $\beta'$-SnTe is the

12: most stable among all possible 2D phases of SnTe including those experimentally

13: available phases. Further, $\beta'$ phases of SnSe and SnS are also found

14: energetically close to the most stable phases. High thermoelectronic (TE) performance

15: has been achieved in the $\beta'$-SnX phases, which have dimensionless figure of

16: merit (ZT) as high as $\sim$0.96 to 3.81 for SnTe, $\sim$0.93 to 2.51 for SnSe and

17: $\sim$1.19 to 3.18 for SnS at temperature ranging from 300 K to 900 K with practically

18: attainable carrier concentration of 5$\times$10$^{12}$ cm$^{-2}$. The high TE

19: performance is resulted from a high power factor

20: which is attributed to the quantum confinement of 2D materials and the band convergence

21: near Fermi level, as well as low thermal conductivity mainly from both low elastic

22: constants due to weak inter-Sn bonding strength and strong lattice anharmonicity.

23: \end{abstract}